Custom Tokens
|
Brass |
Gauge |
5K |
10K |
25K |
||
0.800" |
14 |
|||||
0.880" |
15 |
|||||
0.900" |
15 |
|||||
0.984" |
16 |
|||||
1.000" |
16 |
|||||
1.073" |
14 |
|||||
1.125" |
14 |
Nickel Plated |
Gauge |
5K |
10K |
25K |
||
0.800" |
14 |
|||||
0.880" |
15 |
|||||
0.900" |
15 |
|||||
0.984" |
16 |
|||||
1.000" |
16 |
|||||
1.073" |
14 |
|||||
1.125" |
14 |
Today's Date NORMAL PRODUCTION: |
_____________________________________________________________ Custom Challenge Coins |
Cent (Penny) (United States) |
|
---|---|
Value: |
0.01 U.S. dollar |
Mass: |
2.5 g (0.080 troy oz) |
Diameter: |
19.05 mm (0.750 in) |
Thickness: |
1.55 mm (0.061 in) |
Edge: |
Plain |
Composition: |
Copper-plated zinc 97.5% Zn, 2.5% Cu |
Nickel (United States) |
|
---|---|
Value: |
0.05 U.S. dollar |
Mass: |
5.000 g (0.1615 troy oz) |
Diameter: |
21.21 mm (0.835 in) |
Thickness: |
1.95 mm (0.077 in) |
Edge: |
plain |
Composition: |
75% Cu 25% Ni "Wartime Nickels" From mid-1942 to 1945 56% Cu 35% Ag 9% Mn |
Dime (United States) |
|
---|---|
Value: |
0.1 U.S. dollar |
Mass: |
2.268 g (0.0729 troy oz) |
Diameter: |
17.91 mm (0.705 in) |
Thickness: |
1.35 mm (0.053 in) |
Edge: |
118 reeds |
Composition: |
91.67% Cu 8.33% Ni |
Quarter Dollar (United States) |
|
---|---|
Value: | 0.25 U.S. dollar |
Mass: | 5.670 g (0.182 troy oz) |
Diameter: | 24.26 mm (0.955 in) |
Thickness: | 1.75 mm (0.069 in) |
Edge: | 119 reeds |
Composition: | 91.67% Cu 8.33% Ni |
Half Dollar (United States) |
|
---|---|
Value: | 0.50 U.S. dollar |
Mass: | 11.340 g (0.365 troy oz) |
Diameter: | 30.61 mm (1.205 in) |
Thickness: | 2.15 mm (0.085 in) |
Edge: | 150 reeds |
Composition: | 91.67% Cu 8.33% Ni |
Dollar (United States) |
|
---|---|
Value: | 1 U.S. dollar |
Mass: | 8.100 g (0.260 troy oz) |
Diameter: | 26.5 mm (1.043 in) |
Thickness: | 2.00 mm (0.079 in) |
Edge: | Plain w/ incused inscriptions |
Composition: | 88.5% Cu 6% Zn 3.5% Mn 2% Ni |